Unsaturated Polyester Resin AP112
دوشنبه 16 اسفند 1400
بازدید: 4680
AP112 is an orthophthalic polyester resin. Orthophthalic polyester resin is the standard economic resin with low shrinkage and the most widely used resin system, particularly in the sculpture industry. This resin is dissolved in styrene.
Applications and Fabrication Techniques
. They are specifically formulated for FRP application, figurine casting, stone craft and others
. Sculpture industries
| مشخصه |
میزان |
واحد |
| Colour |
<2 gardner |
|
| Density, 25°C/77°F |
1.06 ± 0.04 g/cm3 |
|
| Dynamic Viscosity, 25°C/77°F |
300-600 cP |
|
| Styrene Content |
35-43 % |
|
| Acid Value |
Max 40 mg KOH/g |
|
| Shelf Life, Dark, 25°C/77°F |
6 months |
|
Typical properties are not to be construed as specifications.
| عنوان |
وزن |
| Resin Temperature |
25°C/77°F |
| Catalyst |
1 (phr)(2) |
| Cobalt octoate1% |
1 (phr) |
| Gel Time (min.) |
5-25 (3) |
Use MEKP 9.9 % Active, O (e.g. AKZO M60 or equivalent peroxide system) as catalyst and Cobalt octoat-1%
phr = parts per hundred resin molding compound
Gel time would be adjustable as request
| مشخصه |
میزان |
واحد |
استاندارد روش آزمون |
| Tensile Strength (MPa) |
Min. 70.0 |
|
ASTM D638 |
| Tensile Elongation (%) |
Min. 2.8 |
|
ASTM D638 |
| Tensile Modulus (GPa) |
Min. 3.0 |
|
ASTM D638 |
| Flexural Strength (MPa) |
Min. 110.0 |
|
ASTM D790 |
| Flexural Modulus (GPa) |
Min. 3.0 |
|
ASTM D790 |
| Heat Distortion Temperature (6) °C |
Min. 70.0 |
|
ASTM D 648 /ISO 75 |
| Barcol Hardness (7) |
Min. 38.0 |
|
ASTM D2583 |
Typical Properties (4) of Post cured (5) Resin Clear Casting:
Typical property values only, not to be construed as specifications.
Cure schedule: 24 hours at room temperature; 3 hours at 85°C (185°F)
Maximum stress: 1.8 MPa.
Test specimen must be prepared by mold.
Handling and Storage Consideration:
This resin should be stored indoors in the original, unopened and undamaged packaging, in a dry place at temperatures between 5°C and 30°C. The shelf life of styrene containing unsaturated polyester resins will be significantly reduced when exposed to light and/or higher temperatures.
Safety:
This resin contains ingredients which could be harmful if mishandled. Contact with skin and eyes should be avoided and necessary protective equipment and clothing should be worn.