Unsaturated Polyester Resin AP116
سه شنبه 17 اسفند 1400
بازدید: 4565
AP116 is an orthophthalic polyester resin. This resin is dissolved in styrene.
Applications and Fabrication Techniques
Recommended for commercial FRP fabrication processes such as: hand lay-up
Wood glue and wood industries
| مشخصه |
میزان |
واحد |
| Colour |
<2.5 gardner |
|
| Density, 25°C/77°F |
1.06 ± 0.04 g/cm3 |
|
| Dynamic Viscosity, 25°C/77°F |
400-750 cP |
|
| Styrene Content |
40-30 % |
|
| Acid Value |
Max 40 mg KOH/g |
|
| Shelf Life, Dark, 25°C/77°F |
4 months |
|
Typical properties are not to be construed as specifications.
| عنوان |
وزن |
| Resin Temperature |
25°C/77°F |
| Catalyst |
1 (phr)(2) |
| Cobalt octoate1% |
1 (phr) |
| Gel Time (min.) |
5-25 (3) |
Use MEKP 9.9 % Active, O (e.g. AKZO M60 or equivalent peroxide system) as catalyst and Cobalt octoat-1%
phr = parts per hundred resin molding compound
Gel time would be adjustable as request
| مشخصه |
میزان |
واحد |
استاندارد روش آزمون |
| Tensile Strength (MPa) |
Min. 65.0 |
|
ASTM D638 |
| Tensile Elongation (%) |
Min. 3.0 |
|
ASTM D638 |
| Tensile Modulus (GPa) |
Min. 2.8 |
|
ASTM D638 |
| Flexural Strength (MPa) |
Min. 100.0 |
|
ASTM D790 |
| Flexural Modulus (GPa) |
Min. 3.0 |
|
ASTM D790 |
| Heat Distortion Temperature (6) °C |
Min. 65.0 |
|
ASTM D 648 /ISO 75 |
| Barcol Hardness (7) |
Min. 35.0 |
|
ASTM D2583 |
Typical Properties (4) of Post cured (5) Resin Clear Casting:
Typical property values only, not to be construed as specifications.
Cure schedule: 24 hours at room temperature; 3 hours at 85°C (185°F)
Maximum stress: 1.8 MPa.
Test specimen must be prepared by mold.
Handling and Storage Consideration:
This resin should be stored indoors in the original, unopened and undamaged packaging, in a dry place at temperatures between 5°C and 30°C. The shelf life of styrene containing unsaturated polyester resins will be significantly reduced when exposed to light and/or higher temperatures.
Safety:
This resin contains ingredients which could be harmful if mishandled. Contact with skin and eyes should be avoided and necessary protective equipment and clothing should be worn.