Unsaturated Orthophthalic Polyester Resin AP124
شنبه 15 شهریور 1404
بازدید: 133
AP124 is an orthophthalic polyester resin. Orthophthalic polyester resin is the standard economic resin and the most widely used resin system. This resin is dissolved in styrene.
Applications and Fabrication Techniques
Concrete industries
Production of durable parts
This resin is specially formulated for making concrete parts
| مشخصه |
میزان |
واحد |
| Density, 25°C/77°F |
1.06 ± 0.04 g/cm3 |
|
| Dynamic Viscosity, 25°C/77°F |
300-600 cP |
|
| Styrene Content |
35-40 % |
|
| Acid Value |
Max 35 mg KOH/g |
|
| Shelf Life, Dark, 25°C/77°F |
4 months |
|
Typical properties are not to be construed as specifications.
| عنوان |
وزن |
| Resin Temperature |
25°C/77°F |
| Catalyst |
1 (phr)(2) |
| Cobalt octoate1% |
1 (phr) |
| Gel Time (min.) |
10-25 (3) |
Use MEKP 9.9 %Active,O(e.g.AKZO M60 or equivalent peroxide system)as catalyst and Cobalt octoat-1%
phr = parts per hundred resin molding compound
Gel time would be adjustable as request
| مشخصه |
میزان |
واحد |
استاندارد روش آزمون |
| Tensile Strength (MPa) |
Min. 70.0 |
|
ASTM D 638 |
| Tensile Elongation (%) |
Min. 3 |
|
ASTM D 638 |
| Flexural Strength (MPa) |
Min. 100.0 |
|
ASTM D 790 |
| Heat Distortion Temperature (6) °C |
Min. 70.0 |
|
ASTM D 648 /ISO 75 |
| Barcol Hardness (7) |
Min. 38.0 |
|
ASTM D 2583 |
Typical Properties (4) of Post cured (5) Resin Clear Casting
Typical property values only, not to be construed as specifications.
Cure schedule: 24 hours at room temperature; 3 hours at 85°C (185°F)
Maximum stress: 1.8 MPa.
Test specimen must be prepared by mold.
Handling and Storage Consideration
This resin should be stored indoors in the original, unopened and undamaged packaging, in a dry place at temperatures between 5°C and 30°C. The shelf life of styrene containing unsaturated polyester resins will be significantly reduced when exposed to light and/or higher temperatures.
Safety
This resin contains ingredients which could be harmful if mishandled. Contact with skin and eyes should be avoided and necessary protective equipment and clothing should be worn.